the difference between low middle high carbon steel strip

Steel is carbon content between 0.04% -2.3% of the iron-carbon alloys. In order to ensure its toughness and ductility, the carbon content is generally not more than 1.7%. The main elements of steel in addition to iron, carbon, and silicon, manganese, sulfur and phosphorus. Classification of steel variety, which according to the chemical composition of classification can be divided into: 
(1) Carbon steel: a low-carbon steel (C≤0.25%); b carbon steel (C≤0.25 ~ 0.60%); c high-carbon steel (C≤0.60%)... 
(2) Alloy:. A low-alloy steel (the total content of alloying elements ≤5%) b of the alloy (the total content of alloying elements> 5 ~ 10%) c of high alloy steel (alloy elements the total content of> 10%). .

Often called high-carbon steel tool steel, carbon content from 0.60 to 1.70%, can be hardened and tempered. Hammers, crowbars and other carbon steel by 0.75%; cutting tools such as drills, taps, reamers and other carbon steel from 0.90 to 1.00% of. High strength general high carbon steel, widely used for cutting, drilling, lathes, milling machines, and so require high hardness environment.

The amount of carbon in the steel ~ 0.60% 0.25% carbon steel. Have killed steel, semi-killed steel rimmed steel and other products. In addition to carbon also contain small amounts of manganese (0.70% to 1.20%). By Product quality is divided into ordinary carbon steel and high-quality carbon structural steel. Thermal processing and cutting good, poor welding performance. Strength, hardness, higher than the low-carbon steel, and the ductility and toughness below the low-carbon steel. Without heat treatment, the direct use of hot-rolled sheet, cold-drawn materials, may also be used after heat treatment. Quenching, tempering the steel has good mechanical properties. The highest attainable hardness of about HRC55 (HB538), σb is 600 ~ 1100MPa. So at moderate intensity levels for various uses in the steel the most widely used, except as a building material, but also used extensively for the manufacture of various mechanical parts.

Low-carbon steel, also known as mild steel, carbon content from 0.10 to 0.30% of low carbon steel is easy to accept a variety of processing such as forging, welding and cutting, commonly used in the manufacture of chains, rivets, bolts, shafts, etc.