Heat-treated spring steel surface quality analysis

Heat-treated spring steel surface 2.2.1 Mechanism of blue 
Heattreated spring steel surface oxidation treatment, also known as blue is the steel surface layer of a thin oxide film, the thickness of the film is about 

0.5 ~ 1.5um, whose main ingredient is iron oxide (Fe3O4), film color depending on the heat.

Hudong Fu (1965-), male (Han), Jiang Xi Nankang people, rolling engineer, engaged in cold-rolled strip technology, management 
And processing the surface condition of the spring steel material of alloy composition, and operating conditions of the oxidation treatment process; make

 the surface of the strip to form a continuous layer of a stable blue, the surface treatment must be bright before the steel strip, the temperature of the furnace

 uniformly blue, stable running speed of the steel strip, parts of the furnace oxidizing gas remains unchanged. 
2.2 is currently unable to go before the cold rolled strip steel heat treatment oil, quenching furnace knot carbon serious scratch the surface; because no 

protective gas quenching furnace parts, stove seal air leaks when there is a bad, off the surface of the steel strip gray oxide layer; unable to do so bright 

surface. 
2.3 back to the stove in the production of nitrogen to protect the surface of the steel strip bright, nitrogen consumed in large, unstable quality. When the 

production of surface tone processing steel, no ventilation protection, furnace mouth still open, so back to the stove with a blue steel tempering and surface features, because 

more oil into the steel surface hardening, tempering furnace tube in the area of oil and formation of oil mist, furnace process to strip performance-based. Tempering process is different in different strip, no bluing process, let alone process optimization. 
2.4 When demanding special blue steel furnace in blue, blue furnace body short, uneven temperature, plus steel front surface can not be bright blue in

 the hair, blue effect is not ideal, great process changes . 
2.5 In summary currently affecting the surface of blue spring steel heat treatment is mainly due to the quality of heat treatment before spring steel blue 

surface brightness level of the surface of blue gas furnace parts, temperature, blue time. And for the improvement and optimization.